Leafing Aluminium Paste For High Temperature Resistant Coating

Leafing Aluminium Paste For High Temperature Resistant Coating

Best Choice Aluminum Paste ZL-2610

Characteristics:

The leafing aluminum paste has a tight surface,good oxidation resistance,surface covering property and high floating abilities,and thus can reflect almost 100%of visible lights,ultraviolet rays and infrared rays,and show bright chrome effect in the paint film.At the same time, it provide a good shield and protection for the paint film and its matrix materials.

Performance Parameter:

Item	Non volatile content (±2%)	Leafing Value (min%)	Water Coverage (min cm2/g)	Screen analysis (325mesh<%)	Solvent	Moisture content (≤%)
ZL2510	65	80	17000	1.0	HA/MS	0.1
ZL2610	65	80	20000	1.0	HA/MS	0.1

Application:

Marine Coating;

Car Refinishing Paint;

Roof Coating;

Tank and Pipe Coating,

Highly Temperature Coating,

Aerosols,

Leather Finishing Agents.

Storage Notices:

1. Keep it under sealed condition after using to prevent the dissolvent from volatilizing.

2. Keep it away from water,acid and alkaline to prevent the corrosion reaction,which causes the formation of hydrogen.

3. Keep it in a dry place away from direct sunlight,rain or too high temperatures,The temperature should be kept between 15-40 degree.

4. Severe bumping and vibrating druing transportation may cause the aluminum pigments to separate from solvent,please mix it well by stirring it before using it.

5. Unsealed aluminum may become dry and oxidized over time,so please check properly before using it again.